PENGARUH TEMPERATUR AKTIVASI FISIKA TERHADAP KINERJA SUPERKAKASITOR BERBASIS ELEKTRODA KARBON DARI AMPAS SAGU
Abstract
The manufacture of activated carbon based on sago pulp as a super-capacitor cell electrode has been successfully performed. Preparation of activated carbon begins with heating of drying raw materials in the sun and followed by oven drying, pre-carbonization, milling, sieving, chemical activation with 2 M concentration KOH solution, pellet printing, carbonization at 600° C using N2 gas followed by physics activation with temperature variation of 700° C; 750° C; 800° C; 850° C; 900° C using water vapor and polishing of pellets are some of the steps that are followed. Carbon electrode density values for each sample of AC 700, AC 750, AC 800, AC 850, and AC 900 are 0,790 g/cm3, 0,791 g/cm3, 0,795 g/cm3, 0,760 g/cm3, dan 0,754 g/cm3. The SEM results show the shape of the particles formed unoccupied. EDX test results show the percentage of carbon reaches 90.13%. The measurement of electrochemical properties performed by cyclic voltammetry method yielded an optimum specific capacitance of 106 F/g obtained at a temperature of 750° C.
Keywords
Full Text:
PDF (INDONESIA)References
Kotz, R. & Carlen, M. (2000). Principles and applications of electrochemical capacitors. Electrochimica Acta, 45(15-16), 2483-2498.
Itagaki, M., Suzuki, S., Shitanda, I., Watanabe, K., & Nakazawa, H., (2007). Impedance analysis of electrical double layer capacitor with transmission line model. J. Power Sources, 164, 415–424.
Niu, C., Sichel, E. K., Hoch, R., Moy, D., & Tennent, H. (1997). High power electrochemical capacitors based on carbon nanotubes electrodes. Applied Physics Letters, 70.
Kim, C. Y., Jang, A. R., & Cho, K. Y. (2012). Optimization of pore structuresand super capacitor properties of carbon aerogel electrodes. Asian Journal of Chemistry, 24.
Stoller, M. D., Park, S., Yanwu, Z., An, J., & Ruoff, R. S. (2008). G raphene-based ultracapacitors. Nano Letters, 8.
Taer, E., Apriwandi, Sugianto, Yusriwandi, Mustika, W. S., Zulkifli, Taslim, R., Kurniasih, B., Agustino, & Dewi, P. (2017). Comparative Study of CO2 and H2O Activation in the Synthesis of Carbon Electrode for Supercapacitors. The 1st International Conference and Exhibition on
Powder Technology Indonesia. AIP Conf. Proc. 1927, 030036-1–030036-6.
Taer, E., Hartati, S. D., Sugianto, & Taslim, R. (2016). Pengaruh variasi suhu aktivasi fisika terhadap sifat fisis dan elektrokimia elektroda Karbon superkapasitor dari Limbah kulit pisang. Jurnal fisika dan aplikasinya, 1(2), 2541-3392.
Taer, E., Iwantono, Manik, S. T., Taslim, R., Dahlan, D., & Deraman, M. (2014). Preparation of Activated Carbon Monolith Electrodes from Sugarcane Bagasse by Physical and Physicalchemical Activation Process for Supercapacitor Application. Advanced Material Research, 896, 179-182.
Taer, E., Deraman, M., Taslim, R., & Iwantono. (2013). Preparation of binderless activated carbon monolith from pre-carbonization rubber wood sawdust by controlling of carbonization and activation condition. Padjadjaran International Physics Symposium, 1554, 33-37.
Taer, E., Afrianda, A., Taslim, R., & Malik, U. (2017). Pemanfaatan ampas sagu sebagai elektroda karbon Superkapasitor. Jurnal komunikasi indonesia. p-ISSN:1412-2960; e-ISSN: 2579-521X.
Mc Clatchey, W. M., Harley, I., & Elevitch, R. C. (2006). Metroxylon Sp. Ecology papers Inc. London.
Sangaji, I. (2009). Mengoptimalkan Pemanfaatan Ampas Sagu Sebagai Pakan Ruminansia Melalui Biofermentasi dengan Jamur Tiram (Pleurotus ostreatus) dan Amoniasi, Disertasi, Institut Pertanian Bogor, Bogor.
Taer, E., Deraman, M., Thalib, I. A., Awitdrus, A., Hasmi, S. A., & Umar A. A. (2011). Preparation of a Highly Prous Binderless Activated Carbon Monolith from Rubber Wood Saw Dust by a Multi Step Activation Process for Application in Supercapacitors. Int. Journal Electrochem. Sci., 6, 3301.
Taer, E. (2009). Pembangunan Superkapasitor Menggunakan Elektroda Karbon. laporan penelitian FMIPA Universitas Riau,
Pekanbaru.
Nurdiansah, H. & Diah, S. (2013). Pengaruh Variasi Temperatur Karbonisasi dan Temperatur Aktivasi Fisika dari Elektroda Karbon Aktif Tempurung Kelapa dan Tempurung Kluwak Terhadap Nilai Kapasitansi Electric Double Layer Capacitor (EDLC). Jurnal Teknik Pomits, 2, Issn: 2337-3539.
Aripin, H., Lestari, L., Ismail, D., & Sabchevski, S. (2010). Sago Waste Based Activated Carbon Film as an Electrode Material for Electric Double Layer Capacitor. The Open Materials Science Journal, 4, 117-124.
Jankowski, H., Swiatkowski, A., & Choma J. (1991). Active Carbon. Ellis Horwood, London. P. 17, 31-40, 75-77.
Taer, E. (2015). Pembuatan dan karakterisasi sifat fisika green carbon paper tanpa perekat menggunakan limbah biomassa. Seminar nasional fisika, 6, 2476-9398.
Hartoyo, Hudaya, N., & Fadli, (1990). Pembuatan arang aktif dari tempurung kelapa dan kayu bakau dengan cara aktivasi uap. Jurnal Penelitian Hasil Hutan, Bogor.8, 8-16. Pusat Penelitian dan Pengembangan Hasil Hutan.
DOI: http://dx.doi.org/10.31258/jkfi.15.2.126-130
Refbacks
- There are currently no refbacks.
![Creative Commons License](http://i.creativecommons.org/l/by-nc/4.0/88x31.png)
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.
Indexing by: