PENGARUH DOPING MANGAN TERHADAP KOMPOSISI DAN SIFAT KRISTALINITAS PARTIKEL OKSIDA BESI PASIR ALAM SUNGAI ROKAN DIPREPARASI DENGAN METODE BALL MILLING

Rahman Kurniawan, Salomo Salomo, Erwin Erwin, Defrianto Defrianto

Abstract


The composition, crystallinity and magnetic susceptibility of nanoparticles in natural sand of the Rokan River, Riau Province have been investigated. After the iron sand separator (ISS) process, the natural sand samples were separated using NdFeB magnets to separate iron oxide particles and other non-ferrous oxides. For 70 hours, the NdFeB product was prepared using the ball milling method to produce BM products. The BM products were ball milled for 30 hours with a manganese doping concentration of 0 wt.%; 5 wt.%, and 10 wt.% produced DM 0, DM 5 and DM 10 products. Magnetic susceptibility values increased based on the values of B0 and BT measured using Pasco Magnetic Probe PS-2162. The results of XRD analysis of DM products contain a hematite phase (α-Fe2O3) which has a hexagonal structure. The crystal size increased along with the increasing concentration of Manganese from 25.494 nm; 25,542 nm to 25.669 nm. The results of XRF analysis of DM products on Fe elements decreased in percentage with increasing Manganese concentration from 18.083%; 15.407% to 12.947%. Other chemical elements such as Si, Al, K, P, Ti, Ca, Ti, Cr, Zn, V and Pb also decreased.


Keywords


Natural Sand; Ball Milling; Doping; X-Ray Diffraction (XRD); X-Ray Fluorescence (XRF)

References


1. Shindharatna, S. D. (2015). Analisis suseptibilitas magnetik sedimen Sungai Metro Kota Malang sebagai indikator pencemaran. Doctoral dissertation, Universitas Negeri Malang.

2. Anggraini, M. S., Ramli, R., & Hidayati, H. (2017). Pengaruh waktu milling terhadap struktur kristal magnetit (Fe3O4) berbahan mineral vulkanik dari Gunung Marapi Sumatera Barat. Pillar of Physics, 10(1), 47-54.

3. Teja, A. S., & Koh, P. Y. (2009). Synthesis, properties, and applications of magnetic iron oxide nanoparticles. Progress in crystal growth and characterization of materials, 55(1-2), 22-45.

4. Wang, Z., Liu, Y., & Zeng, X. (2006). One-step synthesis of γ-Fe2O3 nanoparticles by laser ablation. Powder technology, 161(1), 65-68.

5. Gandha, K., Mohapatra, J., Poudyal, N., Elkins, K., & Liu, J. P. (2017). Enhanced coercivity in Co-doped α-Fe2O3 cubic nanocrystal assemblies prepared via a magnetic field-assisted hydrothermal synthesis. AIP Advances, 7(5), 056324.

6. Malviya, K. D., Dotan, H., Shlenkevich, D., Tsyganok, A., Mor, H., & Rothschild, A. (2016). Systematic comparison of different dopants in thin film hematite (α-Fe 2 O 3) photoanodes for solar water splitting. Journal of Materials Chemistry A, 4(8), 3091-3099.

7. Syafiudin, I. (2016). Pengaruh Kadar Mangan (Mn) Terhadap Struktur Mikro Dan Kekerasan Baja Paduan Fe-17cr-Xmn Melalui Metode Peleburan. Doctoral dissertation, Institut Teknologi Sepuluh Nopember.

8. Djaprie, S., Hardani, H. W., Simarmata, S. L., Smallman, R. E., & Bishop, R. J. (2000). Metalurgi Fisik Modern Dan Rekayasa Material Edisi Keenam. Jakarta: Erlangga.

9. Sinuraya, S., Amiruddin, E., Nurrohmah, D., & Wulandari, T. (2021). Analisa Perubahan Suseptibilitas Magnetik dan Komposisi Partikel Pasir Alam Sungai Rokan sebagai Fungsi Kecepatan Putar Tabung Ball Milling. Komunikasi Fisika Indonesia, 18(3), 225-229.

10. Alisna, S., & Sinuraya, S. (2021). Pemetaan Suseptibilitas Magnetik dan Penentuan Kandungan Logam pada Air Gambut di Kelurahan Tuah Madani Kecamatan Tampan Pekanbaru. Komunikasi Fisika Indonesia, 18(1), 12-17.




DOI: http://dx.doi.org/10.31258/jkfi.19.2.113-118

Refbacks

  • There are currently no refbacks.


Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

Indexing by:

  

 

Image